HartgewebeFabric-base laminateHartgewebeHartgewebe
S.F. Components GmbH

Piston-, rod guide elements of fabric-based laminates

Guide rings of fabric-based laminates (fabric composites) are used for pistons and rods serving to prevent mechanical contact between the moving components and absorbing any side loads that occur.

As guide rings they are used predominantly in heavy-duty hydraulic cylinders.

Depending on the materials selected for the fabric-based laminates, certain combinations can offer excellent friction behavior, outstanding wear properties, stick-slip-free operation and extremely high load-bearing capacities as well as exceptional elasticity and good media resistance.

Rings of fabric-based laminates are manufactured from tubing and feature a preload especially aligned to the piston and/or rod. They are supplied ready to fit to the piston or rod.

The profile is rectangular with beveled or rounded edges in order to prevent impermissible edge compression at the groove corners and to facilitate installation in the groove.

The guide rings are supplied ready to fit with a diagonal cut of 45°. A stepped Z-cut and also a straight 90° cut can also be provided if required. The gap necessary to ensure reliable function has already been taken into account in the manufacture of the rings. This gap is necessary in order to avoid undesirable pressure build-up and to compensate for band/ring elongation.

Individual dimensional ranges can also be manufactured in slotted designs, as closed, continuous designs or as bushings.

Benefits

  • Very high compressive strength
  • High side load absorption capacity
  • Minimal friction and wear
  • Good sliding and emergency running properties
  • High service lifetimes, extremely abrasion-resistant
  • Good chemical resistance
  • Foreign particle embedding capability
  • Easy fitting by snapping into the groove

 

Applications

Velocity:reciprocating up to 1 m/s
Temperature:- 50° C to + 120° C
Stat. compressive strength:from 270  to 345 N/mm²

 

Compressive strength depends on material combination

 

Material

KT-100 is a phenolic resin laminated fabric made up of impregnated cotton fabric made up of impregnated cotton fabric webs.
Static compressive strength vertical to the layered structure: 270 N/mm2

KT-107
is a phenolic resin laminated fabric made up of impregnated cotton fabric webs, additional lubricate graphite.
Static compressive strength vertical to the layered structure: 300 N/mm2

KT-200, KT-200T
, is a phenolic resin-bonded artificial fibre laminated fabric with embedded PTFE. This material exhibits very high load-bearing capacity, outstanding sliding properties and is characterized by its extremely high resilience. The material undergoes no swelling, and water absorption is very low. The KT-200T as stock lenght, is pressed of plate material.
Static compressive strength vertical to the layered structure: 330 N/mm2; KT-200T  320 N/mm2

 

KT-200B, is a epoxy resin-bonded polyester fibre laminated fabric. This material exhibits high load-bearing capacity, outstanding sliding properties and is characterized by its extremely high resilience. The material undergoes no swelling, and water absorption is  negligible. This type of material is available very fast, in small quantity.

Static compressive strength vertical to the layered structure: 310 N/mm2;

 

KT-700, KT700T it´s a combination of aramid fabric and a high temp. modif. phenolic resin, with additional lubrication graphite. This material exhibits very high load-bearing capacity and a high temperature range. This material is also available in stock length.
Static compressive strength vertical to the layered structure: 350 N/mm2; KT-700T  350 N/mm2

 

KT-500T, KT500TS is a combination of polyester and polyester resin, additional lubrication graphite or PTFE. This fabric-based laminate exhibits high load-bearing capacity, high wear resistance and is characterized by very good elastic properties. This material is available both as spiral version in different diameters or as stock lenght.
Static compressive strength vertical to the layered structure: 340 N/mm2

Manufacturing ranges

Inside diameterfrom 12 to 500 mm
Wall thicknessfrom 1,5 to 25 mm
Widthsfrom 3 mm
Tolerances0,03 mm to 0,08 mm

 

The materials KT-100, KT-107 and KT-200 can be used to manufacture fittings and bushings to individual specifications.

Standard design: Diagonal cut
Special design: Straight 90° cut

Directives

All information and values stated concerning our product portfolio are based on the knowledge optained through a long experience of manufacturing and application.
These figures are for indicative purposes only and may vary (exceed or deceed) according to the particular circumstances. Unknown factors in the applications and practice can considerably change the conditions and reduce and change statements, which may cause the above information to be invalid.
No liability can be accepted for any mistakes or omissions, error and subject to change without prior notice.

News

Certification in ISO 9001:2015 with S.F. Components successfully completed

7 November 2018                          S.F. Components successfully completed the Certification of the

[подробнее]
S.F. Hannover Fairs, 2017

April 2017        The world's foremost technology event, HANNOVER MESSE 2017, ended again with a very good outcome. For S.F. Components it has been a very successful week

[подробнее]

SERVICE

Technical information

Guiding elements general

Download

 

Implementation

Download

 

HGW

Download

 

PTFE

Download

 

Polyacetal / POM

Download

© Copyright 2019 S.F. Components GmbH. All rights reserved

This website uses cookies

This website uses cookies to improve user experience. By using our website you consent to all cookies in accordance with our Cookie Policy.